Currently reading: Aluminium Diffraction Pattern by ProSciTech Pty Ltd

Aluminium Diffraction Pattern

User notes for diffraction standard - evaporated Aluminium, S619.

S619Aluminium Diffraction Pattern
In order to use a standard in electron diffraction properly, several conditions are necessary:

  1. After obtaining the pattern of an unknown, it is necessary to expose the known standard to the same
    electrical and magnetic conditions, specifically the same lens current or high voltage.
  2. The specimen must be in the same position as the unknown had been. Small movements of the
    stage are permissible in order to obtain a clearer pattern of the standard.

After developing the diffraction plates, the standard is measured first. The indices are assigned per the
attached ASTM "d" spacings. After assigning the spacings, calculate "K" using the formula K = Sd;
where "K" is a constant that represents wave length of the beam, camera length and associated
variable crystallographic data, "S" is the diameter of the ring in centimeters and "d" is the interplanar
spacing in angstroms. The values for "K" for the first five lines should be within 1% of each other.
Use the mean value of "K".

Next, the pattern of the unknown is measured, and using "K", determined from the standard, the "d"
spacings of the unknown are calculated. It is then necessary to establish identity of the unknown from
the ASTM published data.

Aluminium: ASTM "d" spacings

Miller
Indices hk1
Lattice
Spacing d (Å)
Intensity
I
Lattice Constant
a (Å)
1112.3381004.050
2002.024474.048
2201.431224.047
3111.221244.0489
2221.169074.0495
4001.012424.0496
3310.928984.0490
420.905584.0495
422.826684.0495

Average unit cell from last five lines..............................4.0494